>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Vaughn Simon on June 9, 2007, 9:52 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by on June 10, 2007, 7:24 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by john on June 9, 2007, 3:23 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ignoramus22311 on June 9, 2007, 10:00 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Vacuum pump question | March 6, 2008, 11:19 pm |
| Re: Vacuum pump question | March 10, 2008, 1:22 am |
| fa - here's a project for someone who needs a vacuum pump | July 1, 2008, 2:24 am |
| FA - nice 3 phase 220/440 vacuum pump | April 29, 2006, 6:32 pm |
| Vacuum pump advice please, for casting, investing, etc. | April 16, 2006, 7:30 pm |
| Semi-OT Diesel Pusher, Electric Vacuum Pump, question | January 20, 2007, 7:47 pm |
| Re: OT - use of a pneumatic vacuum pump (auto A/C use), converting R12 manifold gages to R134A? | April 25, 2008, 2:27 am |
| FA: hydraulic pump, right angle gear drive, very heavy caster, Oil pump from large milling machine | April 26, 2006, 1:29 am |
| When to run oiler pump during CNC cycle? Bed lift due to oiler pump. | October 27, 2006, 3:34 pm |
| Dusty wet / dry vacuum | November 25, 2006, 7:10 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore