Posted by Carl McIver on September 29, 2006, 11:21 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Grant Erwin on September 30, 2006, 12:26 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Richard J Kinch on September 30, 2006, 12:34 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ignoramus22416 on September 30, 2006, 12:39 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Tom Gardner on September 30, 2006, 3:43 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Re: HELP Designing lathe spindle, bearings questions, WTB: Lathe headstocks | July 2, 2006, 9:53 pm |
| Continuing lathe chatter (from people now, not the lathe. :-) | May 21, 2008, 1:19 am |
| Re: Continuing lathe chatter (from people now, not the lathe. :-) | May 25, 2008, 12:12 am |
| Re: Continuing lathe chatter (from people now, not the lathe. :-) | June 1, 2008, 11:51 am |
| Re: Continuing lathe chatter (from people now, not the lathe. :-) | June 2, 2008, 10:13 pm |
| Re: Continuing lathe chatter (from people now, not the lathe. :-) | June 9, 2008, 9:48 pm |
| Re: Lathe Oil used | August 15, 2006, 6:30 pm |
| Re: Lathe Oil used | August 16, 2006, 8:19 am |
| 7" by 10" HF lathe | November 2, 2006, 9:13 pm |
| Got me my first lathe! | February 1, 2007, 11:50 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore