Posted by Jerry Foster on September 6, 2007, 12:58 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Silicon Sam on September 6, 2007, 2:16 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Grant Erwin on September 6, 2007, 4:34 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by RoyJ on September 6, 2007, 10:18 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by engineman1@aol.com on September 6, 2007, 4:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Got some welders..maybe F/s | November 17, 2006, 3:25 am |
| Confused about TIG welders | October 22, 2006, 11:21 pm |
| F/S Welders-update | November 19, 2006, 5:03 am |
| Stud welders? | January 27, 2007, 12:54 pm |
| Small Welders | July 28, 2007, 11:27 am |
| stud welders (automotive) | April 11, 2006, 1:32 am |
| Where Have All the Welders Gone, As Manufacturing and Repair Boom? | August 20, 2006, 11:40 am |
| Re: Where Have All the Welders Gone, As Manufacturing and Repair Boom? | August 26, 2006, 4:33 pm |
| Lincoln SP series mig welders versus a retail version? | September 27, 2007, 5:09 am |
| Band saw blades, welding vs brazing, and home made resistance welders? | September 19, 2008, 9:05 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore