Posted by Billy Hiebert on January 12, 2007, 11:36 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by James Waldby on January 12, 2007, 9:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Leon Fisk on January 12, 2007, 4:18 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Mick on January 13, 2007, 1:36 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by F. George McDuffee on January 13, 2007, 8:02 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Re: What happened to it? March 16, 2006, 6:59 pm
excavator through the bridge over the free way, what happened? March 22, 2008, 8:52 am
[OT] Hezbollah Didn't Win -- Arab writers are beginning to lift the veil on what really happened in Lebanon August 28, 2006, 9:34 am
Re: Another 4-start thread question - 1/4" internal thread April 2, 2006, 5:25 pm
class of thread fit on studs and all-thread January 23, 2007, 10:18 am
Thread help September 29, 2006, 10:20 am
What Thread...THANKS November 7, 2006, 4:48 am
thread adapter October 30, 2006, 2:25 pm
How can I do this 3 lead thread? November 15, 2006, 12:07 pm
Help With Go/No Go Thread Ring December 17, 2006, 7:10 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap