Posted by Bart D. Hull on November 21, 2006, 10:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Mark Rand on November 22, 2006, 12:11 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by on November 22, 2006, 4:08 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by werty on November 22, 2006, 9:25 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.