Posted by Tom Gardner on July 14, 2006, 6:25 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by =?ISO-8859-1?Q?Nick_M=FCller?= on July 14, 2006, 8:16 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner on July 14, 2006, 12:13 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner on July 14, 2006, 12:13 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Tom Gardner on July 14, 2006, 1:28 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | UPDATE AND THANKS Milling on the lathe Vertical tslot table or vertical milling vise? | April 1, 2006, 1:55 pm |
| Dimensioning and milling strategy for a rotary table | October 21, 2007, 5:58 pm |
| FA: Universal Wet/Dry Table Saw | March 21, 2007, 3:17 am |
| Monarch Table Saw | September 13, 2007, 2:06 am |
| BP table question | November 4, 2007, 6:53 pm |
| Die lift table | October 5, 2008, 4:49 pm |
| WTD: Servo Table Feed | July 23, 2006, 12:36 pm |
| Emco rotary table. | September 10, 2006, 4:20 pm |
| Who wanted the Oliver table saw? | September 16, 2006, 1:26 pm |
| Good deal on X/Y table? | November 5, 2006, 1:36 pm |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore