>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Christopher Tidy on March 18, 2007, 9:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by JCam on March 18, 2007, 10:18 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by DoN. Nichols on March 18, 2007, 11:21 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Proctologically Violated©® on March 19, 2007, 10:58 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | how to best sell my lathe, grinder, bandsaw and power hacksaw | September 15, 2008, 7:36 pm |
| we accept them, then we once regret Gul and Gavin's short-term cassette | August 12, 2007, 11:24 pm |
| Accept paypal ,wholesale Leisure Shoes (www.urbanwearsneakers.com) | November 9, 2007, 10:50 pm |
| Accept paypal ,wholesale Leisure Shoes(www.urbanwearsneakers.com) | November 10, 2007, 9:51 pm |
| Let's accept no matter how the wrong plants, but don't double the evil locks. | December 4, 2007, 6:10 pm |
| WTB 220 /240 Vac 3 ph AFC, 1 ph input | October 31, 2007, 2:58 pm |
| OT: HDMI tv input from pc | September 17, 2008, 9:47 pm |
| DRO suggestions (computer input like via USB) | June 11, 2007, 10:20 pm |
| Maify sez "We line the experimental input." | August 16, 2007, 12:30 am |
| OT: More power from Microwave oven - Power to melt metal? | January 28, 2007, 1:19 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore