>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Grant Erwin on August 16, 2006, 10:35 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ignoramus31101 on August 16, 2006, 10:37 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Grant Erwin on August 16, 2006, 11:15 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Steve Smith on August 16, 2006, 9:21 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Cinncinnati Mill info wanted | July 18, 2007, 5:24 pm |
| OT: Info on contact grill /sandwich makers wanted | October 14, 2008, 10:05 pm |
| WANTED: Hardinge HNC parts, docs, info, ... Ballscrews, bearings, ... | October 17, 2006, 4:30 pm |
| A hydraulics question | June 17, 2007, 2:38 pm |
| hydraulics; leaking? | April 2, 2008, 1:57 am |
| Hydraulics ,Pneumatics & Controls for Automation & Commercial Applications | March 5, 2007, 8:51 pm |
| backyard "hydraulics design for amateurs" - tilt trailer cylinder | August 4, 2007, 9:35 am |
| Wanted | December 15, 2006, 12:50 am |
| Whoever wanted a 4-48 tap | November 10, 2007, 3:25 pm |
| Re: Just wanted to say thanks.... | September 27, 2008, 2:11 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore