Posted by dave on August 4, 2007, 9:35 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Trevor Jones on August 4, 2007, 10:28 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Andy Asberry on August 4, 2007, 10:53 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Trevor Jones on August 4, 2007, 11:43 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Leo Lichtman on August 5, 2007, 1:11 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Serious trailer design questions | January 12, 2007, 11:57 am |
| Serious trailer design questions (bought AXLE, see pix) | January 13, 2007, 1:32 pm |
| Electro-erosion for amateurs? | February 21, 2007, 6:48 pm |
| 3D Design CAD, 3DESIGN Boutique, other Jewelry design Software, other | January 17, 2008, 1:18 am |
| A hydraulics question | June 17, 2007, 2:38 pm |
| hydraulics; leaking? | April 2, 2008, 1:57 am |
| air over hydraulics info wanted | August 16, 2006, 10:04 am |
| Hydraulics ,Pneumatics & Controls for Automation & Commercial Applications | March 5, 2007, 8:51 pm |
| Porsche Design Dashboard - Porsche Design Watches | September 8, 2008, 4:55 am |
| [Trailer project] Welded adjustable towing eye holder to trailer tongue | January 21, 2007, 6:13 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore