collet chuck help joebass 02-20-2007
Posted by joebass on February 20, 2007, 7:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Eli_S on February 20, 2007, 10:46 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by DoN. Nichols on February 21, 2007, 12:54 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Mawdeeb on February 21, 2007, 3:18 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Stealth Pilot on February 21, 2007, 8:43 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Bison 5C collet chuck vs. Kalamazoo 1CC collet chuck vs. drawtube / collet closer August 1, 2007, 4:26 pm
Re: Chuck Key for Lodge & Shipley Collet Chuck August 26, 2006, 4:43 pm
FA: New Bison 5C "Set-Tru" Collet Chuck July 18, 2006, 6:28 pm
Bison R8 ER-16 collet chuck July 13, 2007, 11:15 pm
MT3 Collet Chuck Runout April 11, 2006, 9:58 pm
FA - collet chuck NMTB-40 - no idea what collets it uses though November 11, 2006, 6:28 pm
Setting up job in 3 jaw chuck. Do you think I should machine chuck jaws??? January 30, 2007, 5:32 am
JC-2 collet July 1, 2007, 8:59 pm
5C collet dimensions October 23, 2006, 9:38 am
ER vs DA vs ?? collet systems June 26, 2007, 12:01 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap