question about aluminum sheet treebeard 12-17-2006
Posted by Ed Huntress on December 17, 2006, 9:47 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Martin H. Eastburn on December 17, 2006, 9:54 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Martin H. Eastburn on December 17, 2006, 9:56 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ed Huntress on December 17, 2006, 10:14 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by treebeard on December 18, 2006, 7:17 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Re: How to saw up a 4'x6' sheet of 5/8" T6 aluminum? June 29, 2006, 2:00 pm
Pre-anodized aluminum sheet? August 17, 2008, 4:14 pm
cutting sheet aluminum on 12 inch wood bandsaw June 19, 2008, 3:27 pm
Cutting Sheet -- Was I asking the wrong question? September 30, 2008, 1:25 pm
Aluminum Question October 23, 2006, 3:01 pm
Machining Aluminum question August 24, 2007, 10:50 pm
Recycling Aluminum cans. A question. September 19, 2007, 6:58 pm
question on bending .040 aluminum on a brake July 24, 2008, 10:09 am
Anodizing Question: Titanium or Aluminum Racks August 18, 2007, 11:28 pm
Re: Question: Temp reached by black anodized aluminum in direct sun January 20, 2008, 12:01 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap