Posted by Cydrome Leader on December 4, 2006, 7:41 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Eric R Snow on December 4, 2006, 8:47 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by on December 6, 2006, 7:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by dcaster@krl.org on December 2, 2006, 12:35 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Cydrome Leader on December 5, 2006, 2:16 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Re: OT? woodgas, engine, induction motor as generator | July 18, 2008, 12:39 am |
| Re: OT? woodgas, engine, induction motor as generator | July 18, 2008, 12:41 am |
| Re: OT? woodgas, engine, induction motor as generator | July 18, 2008, 12:52 am |
| Re: OT? woodgas, engine, induction motor as generator | July 18, 2008, 10:37 am |
| induction heating | November 18, 2006, 9:04 am |
| Induction kWh meter theory | July 9, 2006, 6:43 pm |
| Is HF 45416 a self-excited induction generator? | October 20, 2006, 6:55 am |
| DIY Induction heater for shrinker endmill holders? | April 24, 2008, 3:41 am |
| using a DC motor as a generator, for an AC motor-driven DC welder (pix posted) | May 21, 2008, 4:34 pm |
| Too late the motor is toast :(. Need hints on new motor | September 22, 2007, 11:08 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore