Posted by Robert Barr on January 14, 2007, 5:28 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gordon on January 14, 2007, 5:46 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Robert Barr on January 14, 2007, 7:11 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Tom Gardner on January 14, 2007, 10:18 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gunner on January 15, 2007, 3:55 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Stamping information November 4, 2006, 8:20 pm
STAMPING SHEET METAL April 6, 2007, 2:53 am
tell Catherine it's relative stamping down a dinner August 12, 2007, 5:23 pm
Home sheet metal stamping help needed!!! September 26, 2006, 8:24 pm
Question about stamping or hallmarking and iron temp by color February 16, 2007, 7:14 pm
OT short but interesting update May 17, 2007, 12:39 pm
OT - A short educational filmstrip March 29, 2006, 3:30 pm
Finding 9in diameter CRS in short lengths October 13, 2006, 3:32 pm
Short story about the history of money January 11, 2007, 6:17 pm
Who is it that sells short pieces of metal over the web? August 23, 2007, 3:06 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap