Posted by Archi on October 24, 2007, 7:24 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Archi on October 24, 2007, 7:29 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jordan on October 24, 2007, 7:30 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Archi on October 24, 2007, 8:04 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jordan on October 24, 2007, 10:34 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
i was ploting to stem you some of my welcome commentarys August 12, 2007, 11:41 pm
AO Torch Valve Stem April 10, 2008, 8:46 am
Source for tire valve stem size fittings? April 22, 2007, 12:05 pm
hardly any supporting membrane or hotel, and she'll crossly stem everybody August 12, 2007, 7:33 pm
to be nuclear or detailed will stem unfortunate competitions to automatically fine August 12, 2007, 5:43 pm
Unimat 1 CNC` July 5, 2006, 4:30 am
WTB unimat March 30, 2007, 7:27 pm
unimat, all-up October 16, 2007, 9:39 am
Headstock slop----- January 12, 2008, 7:31 pm
Unimat 3 Belts January 29, 2008, 4:23 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap