very black anodizing dcaster@krl.org 11-04-2006
Posted by dcaster@krl.org on November 4, 2006, 12:10 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Stealth Pilot on November 4, 2006, 7:05 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by dcaster@krl.org on November 4, 2006, 4:37 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Randy Replogle on November 4, 2006, 9:18 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Carl Boyd on November 4, 2006, 9:53 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Anodizing question December 6, 2006, 5:32 pm
anodizing kits? January 5, 2008, 5:46 pm
Large Capacity Anodizing November 3, 2006, 9:37 pm
Removing Aluminum From Anodizing? May 4, 2008, 8:43 pm
Anodizing and Powdercoat Compatibility Questions October 1, 2006, 9:23 pm
Surface roughness after hard anodizing April 19, 2006, 11:26 am
Re: A little plating and anodizing current regulator March 14, 2006, 12:41 am
Re: A little plating and anodizing current regulator March 14, 2006, 2:20 am
Anodizing Question: Titanium or Aluminum Racks August 18, 2007, 11:28 pm
Color change of titanium racks after anodizing September 8, 2007, 5:16 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap