what's happening between blade and steel? gwpm57 10-26-2006
Posted by gwpm57 on October 26, 2006, 11:50 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ignoramus32469 on October 26, 2006, 11:51 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Dave Lyon on October 26, 2006, 11:59 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Emmo on October 26, 2006, 12:04 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Proctologically Violated©® on October 26, 2006, 12:14 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
get your sternly happening knight over my countryside August 12, 2007, 8:19 pm
band saw blade August 3, 2006, 9:32 pm
Band saw blade October 26, 2006, 1:07 pm
HF Blade Welder October 26, 2006, 7:14 pm
Bandsaw blade Q, and tip. April 21, 2007, 10:53 am
WTB Broken band saw blade January 15, 2007, 9:00 am
How to fold a bandsaw blade May 16, 2007, 3:36 pm
Can I save my bandsaw blade? December 27, 2007, 5:21 pm
reciprocating saw blade recycling July 20, 2008, 2:21 pm
Tolerances for grinding a 43" cutter blade October 27, 2006, 2:04 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap